Industrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag Performance

Zhengzhou Rongsheng Refractory Co., Ltd.
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

Industrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag Performance

  • 1
  • 2
  • 3

Brand Name : Rongsheng

Model Number : ML-80A

Certification : CE ISO9001

Place of Origin : China

MOQ : 1 PIECE

Price : USD 540 MT

Payment Terms : L/C, T/T, Western Union

Supply Ability : 1000 TON PER MONTH

Delivery Time : 25 Working Days After Payment

Packaging Details : Fumigation Pallet in size 920*920*1030mm with cardboard and corner protection,waterproof film

AL2O3 : 75%

Apparent Porosity : ≤18%

Cold Crushing Strength : ≥40MPa

0.2MPa Refractoriness Under Load : ≥1600℃

Thermal Shock Resistance 1100℃ : 3%

name : high heat furnace cement

Contact Now

Industrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag Performance

Application:

Mainly used for steel-making basic open hearth and electric furnace bottom and furnace wall, the permanent lining of oxygen converter, non-ferrous metal smelting furnace, high temperature tunnel kiln, calcined magnesite brick and cement rotary kiln lining, furnace bottom and furnace wall, glass kiln regenerator checker brick, etc.

Features:

1. High temperture resistance

2. corrosion resistance

3. High degree of refractoriness,

4. good resistance to alkaline slag,

5. high temperature of load .

6. low thermal shock resistance.

Composition:

Sintered magnesite brick is made of brick and magnesia brick as raw material, after crushing, batching, mixing, molding In 1550 ~ 1600 ℃ high temperature firing, high purity products sintering temperature above 1750 ℃. No magnesia brick is added to the magnesium sand to add proper chemical binding agent, through mixing, molding, drying.

Physical and chemical index:

Items ML-80A
MgO% 80
AL2O3% 5-10
Apparent Porosity% 18
Cold Crushing Strength MPa 40
0.2MPa Refractoriness Under Load ℃ 1600
Thermal Shock Resistance 3

Product Pictures:

Industrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag Performance

Industrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag Performance

Industrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag PerformanceIndustrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag PerformanceIndustrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag PerformanceIndustrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag Performance


Product Tags:

cement kiln bricks

      

fire resistant bricks

      
 Industrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag Performance Manufactures

Industrial Aluminum Silicate Fire Brick , Mullite Bricks With Good Swag Performance Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Zhengzhou Rongsheng Refractory Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 

Friendly Links: www.everychina.com

Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

Copyright © 2009 - 2024 entremaqueros.com. All rights reserved.